X5CrNiCuNb17-4-4, 1.4548, AISI 630, UNS S17400 - Sonraíocht & Feidhm
X5CrNiCuNb17-4-4, 1.4548, AISI 630, UNS S17400 - Sonraíocht & Feidhm
- SAE AMS 5342E (2006) - Cruach, Frithsheasmhach in aghaidh Creimeadh, Teilgin Infheistíochta 16Cr - 4.1Ni - 0.28Cb (Nb) - 3.2Cu Homogenization, Solution, and Chance Heat Treatment (H1100) ) 130 ksi (896 MPa) Neart Teanntachta (17-4)
- SAE AMS 5343E (2006) - Cruach, Frithsheasmhach in aghaidh Creimeadh, Teilgin Infheistíochta 16Cr - 4.1Ni - 0.28Cb (Nb) - 3.2Cu Homogenization, Solution, and Chance Heat Treatment (H1000) ) 150 ksi (1034 MPa) Neart teanntachta (17-4)
- SAE AMS 5344F (2007) - Cruach, Creimeadh-Resistant, Teilgin Infheistíochta 16Cr - 4.1Ni - 0.28Cb - 3.2Cu Homogenization, Réiteach, agus Frasaíocht Teas cóireáilte (H900) 180 ksi (1241 MPa) Neart Teanntachta (17-4)
- SAE AMS 5604G (2013) - Cruach, Frith-Chreimeadh, Leathán, Stiall, agus Pláta 16.5Cr - 4.0Ni - 4.0Cu {{9} }.30Cb Réitigh Teas Chóirithe, Fuaradh Crua-dhian
- SAE AMS 5622F (2013) - Cruach, Frith-chreimeadh, Barraí, Sreangán, Gaibhnithe, Feadáin, agus Fáinní 16Cr - 4.0Ni - 0.30Cb { {9}}.0Cu Réiteach Teas Chóireáilte, Leictreoid Inchaite Frasaíocht Inchaite Leáigh
- SAE AMS 5643/H1150 (2013) - Cruach, Frith-chreimeadh, Barraí, Sreangán, Gaibhnithe, Feadánra agus Fáinní 16Cr – 4.0Ni – 0.30Cb (Nb ) – 4.0Cu Réiteach agus Frasaíocht Teas Chóirithe (H1150)
- SAE AMS 5643S (2013) - Cruach, Frith-chreimeadh, Barraí, Sreangán, Gaibhnithe, Feadáin, agus Fáinní 16Cr - 4.0Ni - 0.30Cb { {9}}.0Cu Réiteach Teas Chóireáilte, Fuaradh Crua-dhéanta
- GA 10088-2 - Cruach dhosmálta. Coinníollacha seachadta teicniúla maidir le leathán/pláta agus stiallacha cruach resistant creimeadh chun críocha ginearálta
Cruach, Creimeadh-Resistant, Teilgin Infheistíochta 16Cr - 4.1Ni - 0.28Cb (Nb) - 3.2Cu Homogenization, Réiteach, agus Teas Déileáiltear le Castacht (H1100) 130 ksi (896 MPa) Neart teanntachta (17-4)
Comhdhéanamh ceimiceach (wt. faoin gcéad ) de X5CrNiCuNb17-4-4, 1.4548, AISI 630, grád UNS S17400: go SAE AMS 5342E (2006)
| Eilimintí | Íosmhéid （ Níos mó ná nó cothrom le ） | Uas. （ Níos lú ná nó cothrom le ） | Cosúil | Nótaí |
|---|
| C | - | 0.07 |
|
|
| Si | - | 1.00 |
|
|
| Mn | - | 1.00 |
|
|
| Cr | 15.00 | 17.50 |
|
|
| Ni | 3.00 | 5.00 |
|
|
| Cu | 3.00 | 5.00 |
|
|
| Nb | 0.15 | 1.45 |
|
|
Airíonna meicniúla de ghrád X5CrNiCuNb17-4-4, 1.4548, AISI 630, grád UNS S17400: go SAE AMS 5342E (2006)
Neart Táirgeachta,Rp 0.2(MPa)
| Coinníoll | Min | uas | Cosúil | Nóta |
|---|
| H900 | 1170 |
|
|
|
| H925 | 1070 |
|
|
|
| H1025 | 1000 |
|
|
|
| H1075 | 860 |
|
|
|
| H1100 | 795 |
|
|
|
| H1150 | 725 |
|
|
|
| H1150M | 520 |
|
|
|
| H1150D | 725 |
|
|
|
Neart teanntachta, Rm(MPa)
| Coinníoll | Min | uas | Cosúil | Nóta |
|---|
| H900 | 1310 |
|
|
|
| H925 | 1170 |
|
|
|
| H1025 | 1070 |
|
|
|
| H1075 | 1000 |
|
|
|
| H1100 | 965 |
|
|
|
| H1150 | 930 |
|
|
|
| H1150M | 795 |
|
|
|
| H1150D | 860 |
|
|
|
Tionchar,Kv/Ku(J)
| Coinníoll | Min | uas | Cosúil | Nóta |
|---|
| H925 | 6.8 |
|
| AKV 21 céim |
| H1025 | 20 |
|
| AKV 21 céim |
| H1075 | 27 |
|
| AKV 21 céim |
| H1100 | 34 |
|
| AKV 21 céim |
| H1150 | 41 |
|
| AKV 21 céim |
| H1150M | 75 |
|
| AKV 21 céim |
| H1150D | 41 |
|
| AKV 21 céim |
Fadú, A( faoin gcéad)
| Coinníoll | Min | uas | Cosúil | Nóta |
|---|
| H900 | 10 |
|
|
|
| H925 | 10 |
|
|
|
| H1025 | 12 |
|
|
|
| H1075 | 13 |
|
|
|
| H1100 | 14 |
|
|
|
| H1150 | 16 |
|
|
|
| H1150M | 18 |
|
|
|
| H1150D | 16 |
|
|
|
Achar a laghdú, ( faoin gcéad )
| Coinníoll | Min | uas | Cosúil | Nóta |
|---|
| H900 | 40 |
|
|
|
| H925 | 44 |
|
|
|
| H1025 | 45 |
|
|
|
| H1075 | 45 |
|
|
|
| H1100 | 45 |
|
|
|
| H1150 | 50 |
|
|
|
| H1150M | 55 |
|
|
|
| H1150D | 50 |
|
|
|
Cruas
| Coinníoll | Cineál | Min | uas | Cosúil | Nóta |
|---|
| A | HRC | 38 |
|
|
|
| A | HB | 363 |
|
|
|
| H900 | HRC | 40 |
|
|
|
| H900 | HB | 388 |
|
|
|
| H925 | HRC | 38 |
|
|
|
| H925 | HB | 375 |
|
|
|
| H1025 | HRC | 35 |
|
|
|
| H1025 | HB | 331 |
|
|
|
| H1075 | HB | 311 |
|
|
|
| H1075 | HRC | 32 |
|
|
|
| H1100 | HRC | 31 |
|
|
|
| H1100 | HB | 302 |
|
|
|
| H1150 | HRC | 28 |
|
|
|
| H1150 | HB | 277 |
|
|
|
| H1150M | HRC | 24 |
|
|
|
| H1150M | HB | 255 |
|
|
|
| H1150D | HRC | 24 |
|
|
|
| H1150D | HB | 255 |
|
|
|
Airíonna fisiceacha de ghrád X5CrNiCuNb17-4-4, 1.4548, AISI 630, UNS S17400 SAE AMS 5342E (2006)
| Cumas teasa, cp20 céim | Nóta |
|---|
| 500 J * kg-1 * K-1 |
|
| Seoltacht teasa, λ | Nóta |
|---|
| 16 W * m-1 * K-1 |
|
| Modal leaisteachas, E | Nóta |
|---|
| 200 GPa |
|
| Dlús | Nóta |
|---|
| 7.85 g/cm3 |
|
| Fachtóir Leathnaithe Líneach, 20 céim | Nóta |
|---|
| 10.9 * 10-6 K-1 |
|
Airíonna gaolmhara
| Cóireáil teasa - Gaibhniú agus rolladh ag 1150 - 900 céim agus fuarú san aer |
| Cóireáil teasa - Anáil ag 1020 - 1055 céim le fuarú in ola nó san aer |
Cóireáil teasa - Ag dul in aois le haghaidh coinníoll móide P800 ag 760 céim san aer ar feadh 2h móide 620 céim san aer ar feadh 4h
|
X5CrNiCuNb17-4-4, 1.4548, AISI 630, UNS S17400 - Sonraí
SAE AMS 5342E (2006) Cruach, Frithsheasmhach in aghaidh Creimeadh, Teilgin Infheistíochta 16Cr - 4.1Ni - 0.28Cb (Nb) - 3.2Cu Homogenization, Solution, and Chance Heat Treatment (H1100) 130 ksi (896 MPa) Neart Teanntachta Cruach chruaite deascadh dhosmálta X5CrNiCuNb17-4-4, 1.4548, AISI 630, UNS S17400 Úsáidtear go hiondúil le haghaidh páirteanna óna dteastaíonn friotaíocht maith creimeadh agus neart suas le 315°C.
Iarratas
Tá cruach cruaite deascadh dhosmálta X5CrNiCuNb17-4-4, 1.4548, AISI 630, UNS S17400 ar cheann de na steels cóimhiotal cróimiam-nicil dhosmálta is coitianta agus is coitianta a úsáidtear le breiseán copair, deascadh cruaite le struchtúr martensitic. Tá sé tréithrithe ag friotaíocht ard creimeadh agus airíonna ard-neart a chothabháil, lena n-áirítear cruas.Is féidir le cruach oibriú sa raon teochta ó -29 céim go 343 céim, agus paraiméadair réasúnta maith á gcoimeád. Ina theannta sin, tá insínteacht réasúnta maith mar shaintréith ag na hábhair sa ghrád seo agus tá a gcuid friotaíocht creimeadh inchomparáide le cruach cruaite deascadh dhosmálta X5CrNiCuNb17-4-4, 1.4548, AISI 630, UNS S17400